Spark plasma sintering and deformation of Ti-TiB2 composites.
Stockholms universitet, Naturvetenskapliga fakulteten, Institutionen för material- och miljökemi (MMK), Avdelningen för materialkemi.
Stockholms universitet, Naturvetenskapliga fakulteten, Institutionen för material- och miljökemi (MMK), Avdelningen för materialkemi.
Stockholms universitet, Naturvetenskapliga fakulteten, Institutionen för material- och miljökemi (MMK), Avdelningen för materialkemi.
2008 (engelsk)Inngår i: Materials Science & Engineering, A: Structural Materials: Properties, Microstructure and Processing, ISSN 0921-5093, Vol. 1-2, nr A475, s. 101-104Artikkel i tidsskrift (Fagfellevurdert) Published
Abstract [en]

Spark plasma sintering (SPS) was used to investigate the densification and deformation behaviour of Ti–TiB2 composites. Fully densified samples were prepared with Ti addition larger than 5%. The prepared composites can be deformed under compression at 1700 °C to achieve a strain of 50% without cracking. At lower temperatures, cracks were initiated due to low ductility of TiB2 and low content of Ti. During the sintering and deformation, TiB is formed via a reaction between Ti and TiB2. To elucidate the formation mechanism of TiB in the SPS process, reactive sintering of TiB using element precursors was also performed. Fully dense samples were prepared but it was not possible to prepare pure uniphase TiB. The reactive sintering resulted in the formation of TiB and TiB2 mixtures at low temperatures and a mixture of TiB2 and Ti3B4 at high temperature

sted, utgiver, år, opplag, sider
Elsevier , 2008. Vol. 1-2, nr A475, s. 101-104
Emneord [en]
Spark plasma sintering; Titanium; Titanium diboride; Grain growth; Reactive sintering
HSV kategori
Identifikatorer
URN: urn:nbn:se:su:diva-17243DOI: 10.1016/j.msea.2007.01.161ISI: 000253693100020OAI: oai:DiVA.org:su-17243DiVA, id: diva2:183764
Tilgjengelig fra: 2009-01-10 Laget: 2009-01-10 Sist oppdatert: 2010-04-26bibliografisk kontrollert
Inngår i avhandling
1. Spark plasma sintering and deformation behaviour of Titanium and Titanium/TiB2Spark plasma sintering and deformation behaviour of Titanium and Titanium/TiB2 composites
Åpne denne publikasjonen i ny fane eller vindu >>Spark plasma sintering and deformation behaviour of Titanium and Titanium/TiB2Spark plasma sintering and deformation behaviour of Titanium and Titanium/TiB2 composites
2007 (engelsk)Licentiatavhandling, med artikler (Annet vitenskapelig)
Abstract [en]

Titanium has been used as a model substance to study how it behaves in a SPS apparatus when heating rate and/or pressure were varied during the sintering and deformation process. The sintering and deformation of Ti in SPS were compared with that occurring in the conventional hot pressing (HP) in order to reveal if there are any positive effects added by the use of SPS. The ductility of Ti was explored in order to understand the sintering and deformation of (Ti) x (TiB2)1-x composites with x = 0.05, 0.1, and 0.2, respectively, expressed in mol ratio. The temperature difference (DT) between the monitored and the temperature that the samples are exposed to was evaluated.

It was noticed that Ti can be sintered at relatively low temperatures. High heating rate implied that the onset temperatures of the sintering and deformation processes decreased. Increasing pressure did not affect the onset temperature but revealed that the deformation of Ti is different if the experiments are conducted within the stability region of the a -phase region of Ti or if the deformation takes place in a temperature region that covers both a-and b-phase areas, i. e. the use of high pressures implied a one step deformation process while the use of low implied that the main part of the deformation took place in the b-phase region.

(Ti) x (TiB2)1-x composites were prepared to full densities at 1500 °C using a holding time of 3 min and pressure of 50 MPa. During the SPS sintering the composite with x= 0.2 revealed the presence of TiB due to the reaction Ti + TiB 2 -> 2TiB while the composites with low x values did not show any formation of TiB. The formation of TiB impaired the mechanical properties. The deformation of composites was very difficult. Their deformability increased with increasing x and temperature as well as pressure. During the deformations of pre-sintered samples TiB was formed in all of the composites.

Publisher
s. 33
Forskningsprogram
materialvetenskap
Identifikatorer
urn:nbn:se:su:diva-26122 (URN)
Presentation
(engelsk)
Opponent
Veileder
Tilgjengelig fra: 2010-01-20 Laget: 2009-03-10 Sist oppdatert: 2010-04-27bibliografisk kontrollert
2. Spark Plasma Sintering Enhancing Grain Sliding, Deformation and Grain Size Control: Studies of the Systems Ti, Ti/TiB2, Na0.5 K0.5 NbO3, and Hydroxyapatite
Åpne denne publikasjonen i ny fane eller vindu >>Spark Plasma Sintering Enhancing Grain Sliding, Deformation and Grain Size Control: Studies of the Systems Ti, Ti/TiB2, Na0.5 K0.5 NbO3, and Hydroxyapatite
2010 (engelsk)Doktoravhandling, med artikler (Annet vitenskapelig)
Abstract [en]

The unique features of the Spark plasma sintering (SPS) were used to investigate the sintering and deformation behaviour of titanium and titanium–titanium diboride composites, and to control the sintering and grain growth of ferroelectric Na0.5K0.5NbO3 (NKN) and of hydroxyapatite (HAp). In the SPS the samples experience a temperature different from that recorded by the thermocouple (pyrometer) used and this temperature difference has been estimated for Ti and NKN.

 

Sintering and deformation of titanium was investigated. Increasing heating rate and/or pressure shifted the sintering to lower temperatures, and the sintering and deformation rates changed when the α→β phase transition temperature was passed. Fully dense Ti/TiB2 composites were prepared. The Ti/TiB2 composites could be deformed at high temperatures, but the hardness decreased due to the formation of TiB. 

 

The kinetic windows within which it is possible to obtain fully dense NKN and HAp ceramics and simultaneously avoid grain growth are defined. Materials have a threshold temperature above which rapid and abnormal grain growth takes place. The abnormal grain growth of NKN is due to a small shift in the stoichiometry, which in turn impairs the ferroelectric properties. Fully transparent HAp nanoceramics was prepared, and between 900 and 1050 oC elongated grains are formed, while above 1050 oC abnormal grain growth takes place.NKN samples containing grains of the sizes 0.35–0.6 µm yielded optimum ferroelectric properties, i.e. a high remanent polarization (Pr = 30 µC/cm2) and high piezoelectric constant (d33= 160 pC/N). The ferroelectric domain structure was studied, and all grains exhibited a multi-domain type of structure.

sted, utgiver, år, opplag, sider
Stockholm: Department of Materials and Environmental Chemistry, Stockholm University, 2010. s. 81
Emneord
Spark plasma sintering, plastic deformation, grain growth, titanium, TiB2, hydroxyapatite, Na0.5K0.5NbO3, ferroelectric, transparent
HSV kategori
Forskningsprogram
materialkemi
Identifikatorer
urn:nbn:se:su:diva-38681 (URN)978-91-7447-072-7 (ISBN)
Disputas
2010-05-25, Magnélisalen, Kemiska övningslaboratoriet, Svante Arrhenius väg 16 B, Stockholm, 13:00 (engelsk)
Opponent
Veileder
Merknad
At the time of doctoral defense the following articles were unpublished and had a status as follows: Article 4: Manuscript; Article 5 : Manuscript Tilgjengelig fra: 2010-05-04 Laget: 2010-04-26 Sist oppdatert: 2010-04-27bibliografisk kontrollert

Open Access i DiVA

Fulltekst mangler i DiVA

Andre lenker

Forlagets fulltekst

Søk i DiVA

Av forfatter/redaktør
Eriksson, MirvaNygren, MatsShen, Zhijian
Av organisasjonen

Søk utenfor DiVA

GoogleGoogle Scholar

doi
urn-nbn

Altmetric

doi
urn-nbn
Totalt: 368 treff
RefereraExporteraLink to record
Permanent link

Direct link
Referera
Referensformat
  • apa
  • ieee
  • modern-language-association-8th-edition
  • vancouver
  • Annet format
Fler format
Språk
  • de-DE
  • en-GB
  • en-US
  • fi-FI
  • nn-NO
  • nn-NB
  • sv-SE
  • Annet språk
Fler språk
Utmatningsformat
  • html
  • text
  • asciidoc
  • rtf