Defects-tolerant Co-Cr-Mo dental alloys prepared by selective laser melting
Stockholm University, Faculty of Science, Department of Materials and Environmental Chemistry (MMK).
Stockholm University, Faculty of Science, Department of Materials and Environmental Chemistry (MMK).
Show others and affiliations
Number of Authors: 6
2015 (English)In: Dental Materials, ISSN 0109-5641, E-ISSN 1879-0097, Vol. 31, no 12, 1435-1444 p.Article in journal (Refereed) Published
Abstract [en]

Objectives. CrCoMo alloy specimens were successfully fabricated using selective laser melting (SLM). The aim of this study was to carefully investigate microstructure of the SLM specimens in order to understand the influence of their structural features inter-grown on different length scales ranging from nano-to macro-levels on their mechanical properties.

Methods. Two different sets of processing parameters developed for building the inner part( core) and the surface (skin) of dental prostheses were tested. Microstructures were characterized by SEM, EBSD and XRD analysis. The elemental distribution was assessed by EDS line profile analysis under TEM. The mechanical properties of the specimens were measured.

Results. The microstructures of both specimens were characterized showing formation of grains comprised of columnar sub-grains with Mo-enrichment at the sub-grain boundaries. Clusters of columnar sub-grains grew coherently along one common crystallographic direction forming much larger single crystal grains which are intercrossing in different directions forming an overall dendrite-like microstructure. Three types of microstructural defects were occasionally observed; small voids (<10 mu m), fine cracks at grain boundaries (<10 mu m) and cracks at weld line boundaries (>10 mu m). Despite the presence of these defects, the yield and the ultimate tensile strength (UTS) were 870 and 430 MPa and 1300 MPa and 1160 MPa, respectively, for the skin and core specimens which are higher than casted dental alloy.

Significance. Although the formation of microstructural defects is hard to be avoided during the SLM process, the SLM CoCrMo alloys can achieve improved mechanical properties than their casted counterparts, implying they are defect-tolerant.

Place, publisher, year, edition, pages
2015. Vol. 31, no 12, 1435-1444 p.
Keyword [en]
SLM, Co-Cr-Mo dental alloy, Microstructure and defects, Mechanical properties
National Category
Industrial Biotechnology Dentistry
Identifiers
URN: urn:nbn:se:su:diva-125792DOI: 10.1016/j.dental.2015.09.003ISI: 000366569800006PubMedID: 26452598OAI: oai:DiVA.org:su-125792DiVA: diva2:944934
Available from: 2016-06-30 Created: 2016-01-18 Last updated: 2016-06-30Bibliographically approved

Open Access in DiVA

No full text

Other links

Publisher's full textPubMed

Search in DiVA

By author/editor
Saeidi, KamranShen, Zhijian
By organisation
Department of Materials and Environmental Chemistry (MMK)
In the same journal
Dental Materials
Industrial BiotechnologyDentistry

Search outside of DiVA

GoogleGoogle Scholar
The number of downloads is the sum of all downloads of full texts. It may include eg previous versions that are now no longer available

Altmetric score

Total: 2 hits
ReferencesLink to record
Permanent link

Direct link